white Aluminum oxide F012

White Fused Alumina F012 is a high purity, synthetic mineral. It is manufactured by the fusion of controlled quality pure grade Bayer Alumina in an electric arc furnace at temperatures greater than 2000 ℃ .

White Aluminum Oxide F012 Chemical Analysis:

ItemContent
Al2O399.50%
SiO20.15%
Fe2O30.03%
Na2O0.30%
CaO0.02%

White Aluminum Oxide  Physical Properties:

ItemContent
ColorWhite
Crystal SystemTrigonal system
Mohs Hardness≥9
Melting Temperature(℃)2250
Refractory Temperature(℃)1900
True Density≥3.5
Grain shapeBlock, with sharp edges
Specific gravityApprox. 3.9 – 4.1 g/cm³
Bulk density(Dependent on grain size)Approx. 1.75 – 1.99g/cm³

White Aluminum Oxide Applications:

• Refractory,casting,foundry etc
• Bonded Abrasives and Coated abrasives
• Creating a matt finish on glass
•  Coated and bonded abrasives grain materials
• Wet and dry blast media, grinding and polishing, etc
• Floor/Wall laminates, Wear-resistant
• Thermal spraying/plasma spraying, Processing very hard
• Catalyst Carrier
• Ceramic and Tiles, Ceramic filter plate, ceramic membrane, etc
• Grinding wheels, Cup wheels, Whetstone, polishing pads, etc
• Blast-cleaning, surface finishing, Deburring, Roughening metallic surfaces

White Aluminum Oxide F012 PSD:

 +2.8MM      0 +2.0MM   ≤20% +1.7MM   ≥45% +1.7MM+1.4MM   ≥70% -1.18MM≤3%

Our Advantages:
1.Professional manufacturer, more than 20 years experiences in the white aluminum oxide.
2.Ensure clients stable quality of white aluminum oxide.
3.Having our own testing laboratory which guarantees products quality
4.Available to deliver samples to clients before place an order. Trail order for testing is also workable.
5.Production capacity: over 40, 000 tons per year.
6.Available to customize according to clients specifications.

Packaging:
1MT big bag or 25kgs bag, Pallet available

25kgs bags in English25kgs bags in Chinese25kgs pvc bags+1mt big bag25kgs pvc bags+pallet
Weight1000 kg
Dimensions100 × 100 × 100 cm
PDF-LOGO-100-.png

TDS not uploaded

PDF-LOGO-100-.png

MSDS not uploaded

Please enter correct URL of your document.

Scroll to Top